Researchers Fabricate New Type of Cellulose Nanopaper

Jun 15, 2018     Email"> PrintText Size

Cellulose nanopaper (CNP) has potential application in the fields of electronic devices, visual display substrates, batteries, barrier material due to its renewability, light-weight, low thermal expansion, excellent mechanical properties and optical properties.

However, CNP is sensitive to moisture due to the hydrophilic nature of cellulose. Absorption of moisture could result in the loss of strength and durability of CNP. These drawbacks limited the usability of CNP under high-moisture environments or in water. To overcome this obstacle, the introduction of expensive building blocks or complicated procedures was usually unavoidable for the fabrication of CNP. 

Recently, a research team led by Dr. LI Bin from the Qingdao Institute of Bioenergy and Bioprocess Technology (QIBEBT) of the Chinese Academy of Sciences extracted lignin-containing cellulose nanofibrils (CNFs) via a one-step recoverable organic acid hydrolysis plus homogenization in dimethylacetamide (DMAC). The resultant CNFs were directly used to fabricate strong, flexible, and water resistant CNP without any complex chemical modification.  

In the obtained CNP, the residual lignin was found to act as a reinforcing agent between CNFs. Results showed that the tensile strength and toughness of the lignin-containing CNP (255 MPa and 19.7 MJ.m-3) were much higher compared with the one without lignin (179 MPa and 12.8 MJ.m-3).

The water-resistance of CNP was also improved extraordinarily, and its maximum wet tensile strength reached up to 83 MPa, which is the highest value in comparison with reported CNP. Moreover, the fabricated CNP exhibited excellent ultraviolet (UV) blocking ability due to the UV-absorbing functional groups of the residual lignin.

The study, published in Journal of Materials Chemistry A, provides a low-cost, clean and sustainable route for the production of lignin-containing CNP, and the characteristics of the resulting CNP demonstrates its potential use in many fields.  

The research was supported by the National Natural Science Foundation of China, the National Science & Technology Pillar Program during the Twelfth Five-Year Plan Period, the Primary Research and Development Plan of Shandong Province, and Shandong Provincial Natural Science Foundation. 


Schematic diagram of the preparation of lignin-containing CNP. (Imaged by WANG Qingbo) 


(Editor: LI Yuan)


Related Articles


Does Microwave Remote Sensing of Soil Moisture Provide Added Values for Short-term Drought Monitoring?

May 29, 2015

Due to the inhomogeneous meteorological forcings of the soil moisture reanalysis that was used to merge the satellite soil moisture retrievals, the ESA CCI merged product was worse than the best reanalysis products in terms of characterizations of shor...

anthropogenic effects;climate change;greenhouse gas;moisture;moisture budget

Detectable Anthropogenic Shift toward Heavy Precipitation over Eastern China

Feb 14, 2017

Anthropogenic forcing has had a detectable and attributable influence on the distribution of daily precipitation amounts over eastern China (EC) during the second half of the twentieth century. The observed shift from weak precipitation to intense prec...

soil lignin;lignin;Badagongshan;lingnin content;chemical signature;plant community

Researchers Reveal Distribution and Characteristics of Soil Lignin in Badagongshan

Jun 30, 2017

Dr. WANG Xinggang under the supervision of Prof. LIU Feng from Wuhan Botanical Garden of Chinese Academy of Sciences chose four major plant communities in subtropical mix forests in Badagongshan (BDGS) National Nature Reserve in central China, i.e. ...

Contact Us

  • 86-10-68597521 (day)
    86-10-68597289 (night)
  • 86-10-68511095 (day)
    86-10-68512458 (night)
  • cas_en@cas.cn
  • 52 Sanlihe Rd., Beijing,
    China (100864)

Copyright © 2002 - Chinese Academy of Sciences